Intro: Objective Hardening teeth on a steel motorcycle gear to a hardness of 48 – 55 HRCMaterial Carbon steel gear 6.9” (175mm) diameterTemperature 2000 F ( 1093 C)Frequency 78 kHzEquipment •UM-HF-90 kW induction heating system, equipped with a remote workhead…

Intro: Objective To quickly heat a steel surgical blade to 2000F (1093C) within 2 seconds so as to harden the blade edge.Material Stainless steel surgical blades, temperature sensing paintTemperature 2000F (1093C)Frequency 339kHzEquipment UM-UHF-6kW induction he

Intro: Overall heat treatment is heating the whole piece, then the appropriate speed cooling, to change its overall mechanical properties of the metal heat treatment process. Roughly the overall heat treatment of steel annealing, normalizing, quenching and tempe

Intro: Objective To heat a titanium rod to 1700F (926.7C) within 60 seconds for hot forming.Material Titanium rods, 1.25”(31.8mm) diameter, 5”(127mm) lengthTemperature 1700F (926.7C)Frequency 70 kHzEquipment • UM-HF-60kW induction heating system, equipped with…

Intro: Objective: To heat a stainless steel “J” tape to 3000F from room temperature at a rate of 15 feet per minute. The material is to be heated to aid in forming the “J” shape from flat stock.Material: Stainless Steel “J” Tape measuring 0.562″ wide, 0.02…

Intro: Objective To heat a metal susceptor vessel to 2200F within 25 minutes for a fiberglass melting applicationMaterial Metal susceptor vesselTemperature 2200FFrequency 300KHZEquipment UM-UHF-60 kW RF power supply, remote heat station and a specially-design

Intro: Induction heating has been used extensively for heat treating processes in a variety of metalworking applications.Some of these applications are associated with discrete parts such as shafts, bearings, gears, and hubs. Here, the most common processes are

Intro: Objective To heat the ends of steel rods to 1800F prior to a forging operation. Processing of the rods includes heating, pressing in a two part die to forge the push rod end, and a final heating in a channel coil to temper the rods and relieve the forging

Intro: Objective To heat titanium rod blanks prior to forging into a turbine blade.Material Titanium rod blanks 0.591″(15.01mm) OD by 11.8″(299.7mm) longTemperature 2030F(1110C)Frequency 64 kHzEquipment • UM-HF-45kW induction heating system equipped with a rem…

Intro: Objective Heat the teeth of a soft steel seatbelt retraction gear to 1700F (926.7C) within two seconds for hardening.Material #4130 steel seatbelt retraction gears, water vortex quenching tank, electronically controlled air valves, adjustable timersTemper